Biomaterials, Zirconia


Article Author:
Arya R


Article Editor:
Kurt Weber


Editors In Chief:
Shane Havens
Jim Wang
Koushik Tripathy


Managing Editors:
Orawan Chaigasame
Carrie Smith
Abdul Waheed
Frank Smeeks
Kristina Soman-Faulkner
Benjamin Eovaldi
Radia Jamil
Sobhan Daneshfar
Saad Nazir
William Gossman
Pritesh Sheth
Hassam Zulfiqar
Navid Mahabadi
Steve Bhimji
John Shell
Matthew Varacallo
Ahmad Malik
Mark Pellegrini
James Hughes
Beata Beatty
Hajira Basit
Phillip Hynes


Updated:
6/18/2019 4:59:48 AM

Introduction

The modern era is known as "Ceramic Age" due to the increasing assortment of ceramic for industrial and medical use. Ceramic materials developed for medical and dental use are termed "bioceramics." The word “zirconium” comes from the Arabic word “zargon” which means “golden in color.” This meaning, in turn, came from the two Persian words "zar," meaning "gold," and "gun," referring to color. German chemist Martin Heinrich Klaproth accidentally discovered zirconium dioxide (ZrO2) in 1789. It was later isolated by the Swedish chemist Jöns Jakob Berzelius in 1824.

ZrO2 is a white crystalline oxide of zirconium found in the minerals baddeleyite and zircon. Zirconium oxide crystals can exist in three phases: (1) the cubic phase (C) which is a square sided straight prism; (2) the tetragonal phase (T) in the form of a rectangular sided straight prism, and (3) the monoclinic phase (M) with a deformed prism with parallelepiped sides. The cubic phase is stable above 2370 degrees Cand with moderate mechanical properties. The tetragonal phase is stable between 1170°C to 2370 °C with improved mechanical properties. The monoclinic phase is stable at room temperature up to 1170°C, with lower mechanical properties, and may contribute to a reduction of the ceramic particles cohesion.

The tetragonal phase can be retained at room temperature by the addition of 3 mol% yttria. Yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) provides mechanical properties superior to other all-ceramic systems due to the tetragonal-to-monoclinic phase transformation. Thus, Y-TZP has been increasingly used as a core material for all-ceramic restorations.[1][2][3]

The advances in CAD/CAM technology made the fabrication of stabilized ZrO2 possible, which could not have been processed by traditional laboratory methods. Thus, over the last decade, zirconia technology has resulted in rapid development of metal-free dentistry that may provide high biocompatibility, enhanced aesthetics, and improved material strength.[4][5][6] 

Function

In the late sixties the progress of research, the use of zirconium as biomaterials was refined. The first use of zirconium oxide for medical purposes was made in 1969 in orthopedic as a new material for hip head replacement instead of titanium or alumina prostheses.

In dentistry, with the development of computer-aided design (CAD)/computeraided manufacturing (CAM) systems, high strength zirconia can be used for the fabrication of crowns, veneers, fixed partial dentures, posts and cores, implants, and implant abutments. In addition, different auxiliary components such as cutting burs and surgical drills, extra-coronal attachments, and orthodontic brackets manufactured using zirconia are available commercially.[7][8][7]

Issues of Concern

Zirconia powder contains small amounts of radioactive impurities from the uranium-radium (226Ra) and thorium (228Th) actinide series. However, zirconia powders with low radioactivity (less than 100 Gyh-1) can be achieved by purifying following appropriate standards.

Heating zirconia at a low temperature (200 to 300 C) can result in the progressive spontaneous transformation of the metastable tetragonal phase into the monoclinic phase in the presence of water, a phenomenon known as low-temperature degradation (LTD). It is a slow transformation that starts in isolated grains on the zirconia surface, leading to an increase in volume. This stresses the adjacent grains and a microcrack appears, allowing water to penetrate and the process to ultimately progress and resulting in a remarkable decrease in strength. This strength degradation is different for various zirconia ceramics, and the variation is related to factors such as stabilizer concentration and distribution, grain size, and the presence of residual stresses. A recent study showed that ceria-stabilized zirconia (12Ce-TZP) was resistant to simulated hydrothermal aging; its flexural strength remained unaffected at a low level of 500 MPa Y-TZP and suffered from low-temperature aging degradation (LTAD) caused by phase transformation.

Aging decreases the physical properties of the material and increases the risk of failure in zirconia restorations. Presence of mechanical stresses and moisture accelerates zirconia aging. Aging leads to changes in the behaviour of the material, weakening it, and subsequently, degrading the material, with microcracks decreasing strength properties.

The grain size influences the mechanical behavior of zirconia, with higher temperatures and longer sintering times producing larger grain sizes. The critical crystal size is approximately 1 micrometer, and zirconia with larger crystals are more prone to spontaneous PTT due to lower stability, whereas a smaller grain size generates favourable properties. It is reported that with grain sizes below 0.2 micrometers, PTT does not increase and fracture toughness decreases.

 The discrepancy of the crown margin adjoined to the pontic was increased by the sintering shrinkage of the bulky pontic in the case of 3-unit and 4-unit frameworks. Therefore, we must beware of distortion of zirconia-based FDPs with long span units when using partially-sintered blocks or green blocks.

Zirconia does not contain silica and thus hydrofluoric acid etching cannot be used. Therefore, other methods of surface treatments are used for zirconia such as grinding/polishing, surface coating, sandblasting, primer treatment, and laser treatment. Sandblasting with aluminium oxide particles results in irregularities and shallow pits in the surface of zirconia, which improves the micromechanical retention. In addition, coating with a 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing silane primer after sandblasting can enhance chemical and micro-mechanical bond strength. 

The selective infiltration etching (SIE) technique also can be used to increase the bond strength of zirconia and resin cement. A glass infiltration agent is heated and is allowed to penetrate the void space between the zirconia grains to re-arrange them. Then the glass infiltration agent is removed using hydrofluoric acid, resulting in the development of inter-grain nano-porosity and generating a relatively rough and reactive surface that exhibits enhanced micro-mechanical bond strength with resin cement. 

One of the technical complications reported in the YTZ-P reconstructions is chipping or delamination of the veneering porcelain. The core-veneer interface is a critical factor in the success of layered restorations. The contributing factors for the fracture may include weakness of the veneer material or the core/veneer bond, stresses and distortion due to the veneering process, unsupported veneering porcelain and configuration of the core and veneer, residual stresses arising from a coefficient of thermal expansion mismatch, and rapid cooling rates after heat treatment.

The use of high-speed polishing rotary instruments is contraindicated for clinical use because of nickel contamination, phase changes in zirconia, and the resultant surface roughness.

Clinical Significance

The restorations are processed either by soft machining of pre-sintered blanks or by hard machining of fully sintered blocks. The mechanical properties of 3Y-TZP are strongly affected by its grain size. Mechanical properties of zirconia have been reported to be higher than other ceramics for dental applications. Fracture resistance of 6–10 MPa/m1/2, a flexural strength of 900–1200 MPa and a compression resistance of 2000 MPa have been reported. Zirconia restorations bear an average load of 755 N. Zirconia yields higher fracture loads than alumina or lithium disilicate.

Zirconia ceramics yield superior wear behavior and lower antagonistic wear compared to porcelain.

The increased opacity of zirconia ceramics could be useful in esthetically demanding clinical situations, such as in cases of masking dichromatic abutment teeth or metal post and cores, but low light transmission may cause inadequate polymerization of resin cement under zirconia ceramics. When comparing different ceramic restorative materials, zirconia ceramics have the highest relative translucency compared to metals.[9]

Bonded all-ceramic restorations provide superior aesthetics because ceramics allow diffuse transmission as well as the diffuse and specular reflectance of light, reproducing a depth of translucency and color that mimics natural teeth. Nevertheless, considering the optical properties, it could be said that yttrium-stabilized zirconia has a high refractive index, low absorption coefficient, and high opacity in the visible and infrared spectra. 

This material is a non-cytotoxic metal oxide, is insoluble in water, and has no potential for bacterial adhesion. In addition, it has radio-opacity properties and exhibits low corrosion. These are inert material and exhibit biocompatibility. Zirconia implants osseointegrate as well as titanium implants.

Y-TZP has a high fracture toughness and a flexural strength. When a crack initiates on the surface of Y-TZP, the stress concentration at the top of the crack causes the tetragonal crystal to transform into a monoclinic crystal, with associated volumetric expansion. In the vicinity of a propagating crack, the stress-induced transformation leads to compressive stress that shields the crack tip from the applied stress and enhances the fracture toughness.

Other Issues

Dimensional changes from the sintering process of Y-TZP can lead to non-uniform cement space in single copings. The manufacturing process of Y-TZP blanks may influence the sintering shrinkage pattern and, consequently, on the prostheses fit.

The production process of these blocks consists of compacting zirconia powder in the presence of a binder through a cold, isostatic pressing process; this leads to the homogeneous distribution of the components inside the block. The pre-sintering temperature of zirconia can influence hardness, machinability, and roughness of the blocks.

Purification processes, new processing methods (CAD-CAM, hot isotactic pressing), and identification allow wide use of zirconia in technical and biological applications. As many new trends and applications for zirconia are being discovered, the future of this biomaterial appears to be very promising.


Interested in Participating?

We are looking for contributors to author, edit, and peer review our vast library of review articles and multiple choice questions. In as little as 2-3 hours you can make a significant contribution to your specialty. In return for a small amount of your time, you will receive free access to all content and you will be published as an author or editor in eBooks, apps, online CME/CE activities, and an online Learning Management System for students, teachers, and program directors that allows access to review materials in over 500 specialties.

Improve Content - Become an Author or Editor

This is an academic project designed to provide inexpensive peer-reviewed Apps, eBooks, and very soon an online CME/CE system to help students identify weaknesses and improve knowledge. We would like you to consider being an author or editor. Please click here to learn more. Thank you for you for your interest, the StatPearls Publishing Editorial Team.

Biomaterials, Zirconia - Questions

Take a quiz of the questions on this article.

Take Quiz
Which is the phase of zirconia stable at room temperature?



Click Your Answer Below


Would you like to access teaching points and more information on this topic?

Improve Content - Become an Author or Editor and get free access to the entire database, free eBooks, as well as free CME/CE as it becomes available. If interested, please click on "Sign Up" to register.

Purchase- Want immediate access to questions, answers, and teaching points? They can be purchased above at Apps and eBooks.


Sign Up
What is the critical temperature range for developing aging in zirconia?



Click Your Answer Below


Would you like to access teaching points and more information on this topic?

Improve Content - Become an Author or Editor and get free access to the entire database, free eBooks, as well as free CME/CE as it becomes available. If interested, please click on "Sign Up" to register.

Purchase- Want immediate access to questions, answers, and teaching points? They can be purchased above at Apps and eBooks.


Sign Up
Which one of the following cannot be used to stabilize zirconia?



Click Your Answer Below


Would you like to access teaching points and more information on this topic?

Improve Content - Become an Author or Editor and get free access to the entire database, free eBooks, as well as free CME/CE as it becomes available. If interested, please click on "Sign Up" to register.

Purchase- Want immediate access to questions, answers, and teaching points? They can be purchased above at Apps and eBooks.


Sign Up

Biomaterials, Zirconia - References

References

Tilden DS,Roy ME,Whiteside LA, Enhanced Adhesion of Plasma-Sprayed Commercially Pure Titanium Porous Coatings to Polished Mg-PSZ Ceramic Substrates. Journal of biomedical materials research. Part A. 2019 Apr 14;     [PubMed]
Spies BC,Balmer M,Jung RE,Sailer I,Vach K,Kohal RJ, All-ceramic single crowns supported by zirconia implants: 5-year results of a prospective multicenter study. Clinical oral implants research. 2019 Apr 10;     [PubMed]
Alraheam IA,Donovan TE,Rodgers B,Boushell L,Sulaiman TA, Effect of masticatory simulation on the translucency of different types of dental zirconia. The Journal of prosthetic dentistry. 2019 Mar 27;     [PubMed]
Faria D,Pires JM,Boccaccini AR,Carvalho O,Silva FS,Mesquita-Guimarães J, Development of novel zirconia implant's materials gradated design with improved bioactive surface. Journal of the mechanical behavior of biomedical materials. 2019 Feb 20;     [PubMed]
Kolakarnprasert N,Kaizer MR,Kim DK,Zhang Y, New multi-layered zirconias: Composition, microstructure and translucency. Dental materials : official publication of the Academy of Dental Materials. 2019 May;     [PubMed]
Jang YS,Nguyen TT,Ko YH,Lee DW,Baik BJ,Lee MH,Bae TS, {i}In vitro{/i} wear behavior between enamel cusp and three aesthetic restorative materials: Zirconia, porcelain, and composite resin. The journal of advanced prosthodontics. 2019 Feb;     [PubMed]
Rodrigues CDS,Aurélio IL,Kaizer MDR,Zhang Y,May LG, Do thermal treatments affect the mechanical behavior of porcelain-veneered zirconia? A systematic review and meta-analysis. Dental materials : official publication of the Academy of Dental Materials. 2019 May;     [PubMed]
Schünemann FH,Galárraga-Vinueza ME,Magini R,Fredel M,Silva F,Souza JCM,Zhang Y,Henriques B, Zirconia surface modifications for implant dentistry. Materials science     [PubMed]
Ramos NC,Kaizer MR,Campos TMB,Kim J,Zhang Y,Melo RM, Silica-Based Infiltrations for Enhanced Zirconia-Resin Interface Toughness. Journal of dental research. 2019 Apr;     [PubMed]

Disclaimer

The intent of StatPearls is to provide practice questions and explanations to assist you in identifying and resolving knowledge deficits. These questions and explanations are not intended to be a source of the knowledge base of all of medicine, nor is it intended to be a board or certification review of Surgery-Ophthalmology. The authors or editors do not warrant the information is complete or accurate. The reader is encouraged to verify each answer and explanation in several references. All drug indications and dosages should be verified before administration.

StatPearls offers the most comprehensive database of free multiple-choice questions with explanations and short review chapters ever developed. This system helps physicians, medical students, dentists, nurses, pharmacists, and allied health professionals identify education deficits and learn new concepts. StatPearls is not a board or certification review system for Surgery-Ophthalmology, it is a learning system that you can use to help improve your knowledge base of medicine for life-long learning. StatPearls will help you identify your weaknesses so that when you are ready to study for a board or certification exam in Surgery-Ophthalmology, you will already be prepared.

Our content is updated continuously through a multi-step peer review process that will help you be prepared and review for a thorough knowledge of Surgery-Ophthalmology. When it is time for the Surgery-Ophthalmology board and certification exam, you will already be ready. Besides online study quizzes, we also publish our peer-reviewed content in eBooks and mobile Apps. We also offer inexpensive CME/CE, so our content can be used to attain education credits while you study Surgery-Ophthalmology.